Influence of Laser Welding Modes along a Curved Path on the Mechanical Properties and Heterogeneity of the Microstructure of 316L Steel Plates.

The results of experimental studies in the manufacture of components of the supporting structure of the first wall panel, carried out as part of the manufacture of a model of the International Thermonuclear Experimental Reactor (ITER) using laser welding technology, are presented. The influence of laser welding modes on the quality of formation, microstructure characteristics, and mechanical properties of a welded joint made of 10 mm thick 316L steel was studied. A coaxial nozzle was designed and manufactured to protect the weld pool with a curved trajectory.

Influence of Laser Beam Wobbling Parameters on Microstructure and Properties of 316L Stainless Steel Multi Passed Repaired Parts.

The results of experimental studies of repair of the supporting structure components made of 316L steel multi-pass laser cladding with filler wire are presented. The influence of the wobbling mode parameters, welding speed, and laser power on the formation of the deposited metal during multi-pass laser cladding with filler wire of 316L steel samples into a narrow slot groove, 6 mm deep and 3 mm wide, are shown. Non-destructive testing, metallographic studies, and mechanical tests of the deposited metal before and after heat treatment (2 h at 450 °C) were carried out.