In vitro and in vivo assessment of squeeze-cast Mg-Zn-Ca-Mn alloys for biomedical applications.

Squeeze casting of biodegradable Mg-4Zn-0.5Ca-xMn (x = 0, 0.4 or 0.

A new magnesium sheet alloy with high tensile properties and room-temperature formability.

Lightweight sheet alloys with superior mechanical performance such as high strength, ductility and formability at room temperature (RT) are desirable for high volume automotive applications. However, ductility or formability of metallic alloys at RT are generally inversely related to strength, thereby making it difficult to optimize all three simultaneously. Here we design a new magnesium sheet alloy-ZAXME11100 (Mg-1.

Three-dimensional cellular automaton simulation of coupled hydrogen porosity and microstructure during solidification of ternary aluminum alloys.

Hydrogen-induced porosity formed during solidification of aluminum-based alloys has been a major issue adversely affecting the performance of solidification products such as castings, welds or additively manufactured components. A three-dimensional cellular automaton model was developed, for the first time, to predict the formation and evolution of hydrogen porosity coupled with grain growth during solidification of a ternary Al-7wt.%Si-0.

Microstructural, mechanical and corrosion characteristics of heat-treated Mg-1.2Zn-0.5Ca (wt%) alloy for use as resorbable bone fixation material.

Mg-Zn-Ca alloys have grabbed most of the recent attention in research attempting to develop an Mg alloy for bone fixation devices due to their superior biocompatibility. However, early resorption and insufficient strength remain the main problems that hinder their use. Heat treatment has previously been thoroughly studied as a post-shaping process, especially after the fabrication of complex parts (e.