Preparation and magnetic properties of multiferroic CuMnO2 nanoparticles.

CuMnO2 nanoparticles with diameters of 64 nm were synthesized by a novel wet chemical method. An optimized two-step annealing method was developed through the analysis of thermogravimetric differential thermal analysis (TG-DTA) measurements in order to obtain single-phase CuMnO2. A sharp exothermic peak was observed in the DTA curve at approximately 500 K where structural changes of the copper oxides and manganese oxides in the precursor are expected to occur.

Characterization of magnetic and dielectric properties of Bi(1-x)Gd(x)FeO3 nanoparticles by local structure analyses.

Bi(1-x)Gd(x)FeO3 (0 < or = x < or = 1.0) nanoparticles were synthesized by a wet chemical method. The annealing temperatures were controlled to obtain single-phase Bi(1-x)Gd(x)FeO3 nanoparticles.