Nano-alumina powders/ceramics derived from aluminum foil waste at low temperature for various industrial applications.

In this work, nanoscale single crystalline γ- and α-alumina powders have been successfully prepared from aluminum foil waste precursor via co-precipitation method using NH4OH as a precipitant. The obtained gel after co-precipitation treatment, was calcined at different temperatures (500,700, 900, 1050, 1100, 1300 and 1500 °C) and the products were characterized by XRD, FTIR and HRTEM. The results revealed that nano-γ-Al2O3 was fully transformed to nanometer-sized α-Al2O3 (36-200 nm) after annealing at temperatures as low as 1100 °C.