Surface Properties of 1DTiO Microrods Modified with Copper (Cu) and Nanocavities.

This work deals with Cu-modified 1DTiO microrods (MRs) and their surface properties. The pristine lyophilized precursor Cu_1DTiO, prepared by an environmentally friendly cryo-lyophilization method, was further annealed in the temperature interval from 500 to 950 °C. The microstructure of all samples was characterized by electron microscopy (SEM/EDS and HRTEM/SAED), X-ray powder diffraction (XRD), infrared spectroscopy, simultaneous DTA/TGA thermoanalytical measurement, and mass spectroscopy (MS).

Iron oxides in human spleen.

Iron is an essential element for fundamental cell functions and a catalyst for chemical reactions. Three samples extracted from the human spleen were investigated by scanning (SEM) and transmission electron microscopy (TEM), Mössbauer spectrometry (MS), and SQUID magnetometry. The sample with diagnosis of hemosiderosis (H) differs from that referring to hereditary spherocytosis and the reference sample.

Temperature-related degradation and colour changes of historic paintings containing vivianite.

Temperature-related degradation of pure synthetic as well as partly oxidised natural vivianite has been studied by high-temperature X-ray diffraction (HT-XRD) covering the whole extent of the temperature-related stability of its structure. While temperatures around 70°C are already damaging to vivianite, exposition to 160°C results in complete amorphisation of both the vivianite and its oxidation products. As indicated by Mössbauer spectroscopy, temperature-induced oxidation of vivianite starts at 90°C.