Fabrication and characterization of Si Ge nanocrystals in as-grown and annealed structures: a comparative study.

Multilayer structures comprising of SiO/SiGe/SiO and containing SiGe nanoparticles were obtained by depositing SiO layers using reactive direct current magnetron sputtering (dcMS), whereas, Si and Ge were co-sputtered using dcMS and high-power impulse magnetron sputtering (HiPIMS). The as-grown structures subsequently underwent rapid thermal annealing (550-900 °C for 1 min) in N ambient atmosphere. The structures were investigated using X-ray diffraction, high-resolution transmission electron microscopy together with spectral photocurrent measurements, to explore structural changes and corresponding properties.

Nanostructuring of GeTiO amorphous films by pulsed laser irradiation.

Laser pulse processing of surfaces and thin films is a useful tool for amorphous thin films crystallization, surface nanostructuring, phase transformation and modification of physical properties of thin films. Here we show the effects of nanostructuring produced at the surface and under the surface of amorphous GeTiO films through laser pulses using fluences of 10-30 mJ/cm(2). The GeTiO films were obtained by RF magnetron sputtering with 50:50 initial atomic ratio of Ge:TiO2.

From synthetic to natural nanoparticles: monitoring the biodegradation of SPIO (P904) into ferritin by electron microscopy.

A strong focus on Superparamagnetic Iron Oxide Nanoparticles (SPIOs) has been appreciated recently especially for their use in Magnetic Resonance Imaging (MRI). However, some questions are being raised over these particles due to their long-term toxicity related to the production of toxic free iron during their biodegradation. Here we show by Electron Microscopy how SPIOs (P904) (Guerbet, Paris) are degraded after they are taken up by macrophages, so that iron from the SPIO core is progressively incorporated into the iron-storing protein ferritin (a nontoxic form of iron).