Temporal evolution and correlation between cooperative luminescence and photodarkening in ytterbium doped silica fibers.

The present work describes photodarkening from the viewpoint of cooperative luminescence. The temporal evolution of both effects was measured simultaneously by means of ytterbium doped aluminosilicate fibers for concentrations up to 1.8 wt% Yb3+.

Concentration dependence and self-similarity of photodarkening losses induced in Yb-doped fibers by comparable excitation.

We report on an extensive investigation of photodarkening in Yb-doped silica fibers. A set of similar fibers, covering a large Yb concentration range, was made so as to compare the photodarkening induced losses. Careful measurements were made to ensure equal and uniform inversion for all the tested fibers.

Casting method for producing low-loss chalcogenide microstructured optical fibers.

We report significant advances in the fabrication of low loss chalcogenide microstructured optical fiber (MOF). This new method, consisting in molding the glass in a silica cast made of capillaries and capillary guides, allows the development of various designs of fibers, such as suspended core, large core or small core MOFs. After removing the cast in a hydrofluoric acid bath, the preform is drawn and the design is controlled using a system applying differential pressure in the holes.

Fabrication of complex structures of Holey Fibers in Chalcogenide glass.

We report recent progress on fabrication of solid core microstructured fibers in chalcogenide glass. Several complex and regular holey fibers from Ga5Ge20Sb10S65 chalcogenide glass have been realized. We demonstrate that the "Stack & Draw" procedure is a powerful tool against crystallisation when used with a very stable chalcogenide glass.