Translucency of monolithic and core zirconia after hydrothermal aging.

: To evaluate the hydrothermal aging effect on the translucency of partially stabilized tetragonal zirconia with yttria (Y-TZP) used as monolithic or fully milled zirconia and of core type. : Twenty disc-shaped specimens (1 and 10 mm) for each type of monolithic and core Y-TZP materials were milled and sintered according to the manufacturer's instruction. The final specimens were divided into two groups according to the type of Y-TZP used.

A new modification for improving shear bond strength and other mechanical properties of conventional glass-ionomer restorative materials.

Purpose: To study the effect of addition of poly(acrylamide-co-sodium acrylate) copolymer and/or TiO2 nanoparticles on the mechanochemical properties of conventional glass ionomer (GIC)-based restorative materials.

Materials And Methods: The copolymer was prepared, characterized and then added, either separately or in combination with different proportions of TiO2 nanoparticles to the conventional GIC powder. The developed composites were characterized using FTIR spectrometry, x-ray diffraction, and scanning electron microscopy.

Influence of pulpotomy medicaments on the ultrastructure and shear bond strength of a self-etch adhesive to primary tooth dentin.

Objective: To compare the effect of the pulpotomy medicaments glutaraldehyde, ferric sulfate, and formocresol on the structure and shear bond strength of a self-etch adhesive to the dentin of primary teeth.

Method And Materials: Forty human primary molars were sectioned mesiodistally and divided into four groups: group I (control group), dentin specimens were soaked in distilled water for 48 hours; group II, dentin specimens were soaked in 2% glutaraldehyde; group III, dentin specimens were soaked in formocresol; and group IV, dentin specimens were soaked in 15.5% ferric sulfate.