Exploring fiberglass post numbers for enhanced fatigue resistance in molars without coronary remnants.

This study aimed to assess the fatigue resistance of molars lacking a coronary remnant, using zero, one, two, or three fiberglass posts. Forty caries/crack-free human molars with coronal portions removed at the pulp chamber floor were randomly allocated into four groups (n=10). Following endodontic treatment, posts (Whitepost DC/DC.

Fatigue resistance of monolithic and multilayer zirconia crowns using veneer layering or CAD-on technique.

This study aims to evaluate the fatigue resistance of monolithic zirconia (Yz) and multilayer ceramic structures using the CAD-on technique in different thicknesses. Fifty (N=50) standardized single crowns preparations were made in fiberglass-reinforced epoxy resin (NEMA grade G10), digitalized, and restorations were machined in CAD-CAM, composing 5 groups (n= 10): Control: 1.5 mm (milled zirconia framework + manual layered porcelain); Yz monolithic 1.

Effect of preheating and ultrasound application of resin-based luting agents on the failure load of a lithium disilicate glass-ceramic.

Purpose: To assess the effect of preheating resin-based materials and ultrasound application on the failure load of a lithium disilicate glass-ceramic.

Materials And Methods: Ninety ceramic specimens were produced (14×12×1.0 mm) and divided into 9 groups (n = 10) to be bonded to a dentin analog (Nema G10) with light-cured luting agent (LC), flowable resin composite (FL), and supra-nano filled resin composite (SN), as follows: LC/R - LC at room temperature; LC/P - preheated LC; LC/P/U - preheated LC and Ultrasound; FL/R - FL at room temperature; FL/P - preheated FL; FL/P/U - preheated FL and Ultrasound; SN/R - SN at room temperature; SN/P - preheated SN; SN/P/U - preheated SN and Ultrasound.

Fatigue Properties of Weakened and Non-weakened Roots Restored with CAD-CAM Milled Fiber Post, Prefabricated Fiber Post, or Cast Metal Post.

Statement Of Problem: Customized glass fiber posts using CAD-CAM technology have been suggested for restoring endodontically treated teeth. However, how weakened or non-weakened roots restored with anatomical CAD-CAM posts behave under cyclic fatigue is not clear.

Objective: To evaluate the load-bearing capacity under fatigue (fatigue failure load [FFL], the number of cycles for failure [CFF], and survival probabilities) and fracture pattern of weakened and non-weakened roots restored with CAD-CAM fiber post and cores, metal cast-post-core, and prefabricated fiber post and resin core.

Do preheated composite resin or adhesive resin layer strengthen the feldspar ceramic?

Statement Of Problem: Preheated composite resin and adhesive coating have been recommended as luting agents for ceramic veneers; however, information about the mechanical behavior of feldspathic porcelain veneers after using these methods is still limited.

Purpose: The purpose of this in vitro study was to evaluate the influence of the use of preheated composite resin or an adhesive resin layer on the strengthening of a feldspathic porcelain.

Material And Methods: Feldspathic porcelain disks were fabricated (N=210), etched (10% hydrofluoric acid for 90 seconds), and bonded according to resin-based luting agents (30 per group) for the biaxial flexural strength tests: photopolymerized resin cement, flowable composite resin, preheated composite resin, with or without previous adhesive coating.