Microstructural Modification of TiAl6V4 Alloy to Avoid Detrimental Effects Due to Selective In Vivo Crevice Corrosion.

TiAl6V4 wrought alloy is a standard material used for endoprostheses due to its ideal characteristics in terms of osseointegration. However, the insufficient wear and crevice corrosion resistance of TiAl6V4 are limiting factors that can cause clinical problems. Therefore, the objective of this study was to analyze and identify suitable phases and microstructural states of TiAl6V4 alloy with advantageous implant properties by thermal treatments.

Microstructure-dependent crevice corrosion damage of implant materials CoCr28Mo6, TiAl6V4 and REX 734 under severe inflammatory conditions.

Fretting corrosion is associated with increased risk of premature implant failure. In this complex in vivo corrosion system, the contribution of static crevice corrosion of the joined metal alloys is still unknown. The aim of this study was to develop a methodology for testing crevice corrosion behavior that simulates the physiological conditions of modular taper junctions and to identify critical factors on corrosion susceptibility.

Modulation of Mammalian Cell Behavior by Nanoporous Glass.

The introduction of novel bioactive materials to manipulate living cell behavior is a crucial topic for biomedical research and tissue engineering. Biomaterials or surface patterns that boost specific cell functions can enable innovative new products in cell culture and diagnostics. This study investigates the influence of the intrinsically nano-patterned surface of nanoporous glass membranes on the behavior of mammalian cells.

Effect of deep rolling on subsurface conditions of CoCr28Mo6 wrought alloy to improve the wear resistance of endoprostheses.

Wear of orthopaedic endoprostheses is associated with adverse local and systemic reactions and can lead to early implant failure. Manufacturing determines the initial subsurface microstructure of an alloy that influences the implant's wear behaviour. Therefore, this study aims at generating enhanced wear resistances by a modification of the surface and subsurface microstructure of a CoCr28Mo6 wrought alloy by applying deep rolling.