Exploring the degradation of silver nanowire networks under thermal stress by coupling X-ray diffraction and electrical resistance measurements.

The thermal instability of silver nanowires (AgNWs) leads to a significant increase of the electrical resistance of AgNW networks. A better understanding of the relationship between the structural and electrical properties of AgNW networks is primordial for their efficient integration as transparent electrodes (TEs) for next-generation flexible optoelectronics. Herein, we investigate the evolution of the main crystallographic parameters ( integrated intensity, interplanar spacing and peak broadening) of two Ag-specific Bragg peaks, (111) and (200), during a thermal ramp up to 400 °C through X-ray diffraction (XRD) measurements, coupled with electrical resistance measurements on the same AgNW network.

Silver Nanowire Networks: Ways to Enhance Their Physical Properties and Stability.

Silver nanowire (AgNW) networks have been intensively investigated in recent years. Thanks to their attractive physical properties in terms of optical transparency and electrical conductivity, as well as their mechanical performance, AgNW networks are promising transparent electrodes (TE) for several devices, such as solar cells, transparent heaters, touch screens or light-emitting devices. However, morphological instabilities, low adhesion to the substrate, surface roughness and ageing issues may limit their broader use and need to be tackled for a successful performance and long working lifetime.

Cellulose nanofibrils and silver nanowires active coatings for the development of antibacterial packaging surfaces.

An active ink composed of cellulose nanofibrils and silver nanowires was deposited on flexible and transparent polymer films using the bar coating process, achieving controlled thicknesses ranging from 200 nm up to 2 μm. For 350 nm thick coating on polyethylene terephthalate films, high transparency (75.6% transmittance) and strong reduction of bacterial growth equal to 89.

A fibrous cellulose paste formulation to manufacture structural parts using 3D printing by extrusion.

An optimized paste based on short natural cellulose fibers combined with carboxymethyl cellulose at a high dry content (42 wt.%) was implemented as a bio-based material for 3D printing by extrusion. The homogeneous paste exhibited a pronounced thinning behavior and yield stress; it was extruded using a screw extrusion-based direct ink writing system and could easily flow through a small nozzle.

Use of nanocellulose in printed electronics: a review.

Since the last decade, interest in cellulose nanomaterials known as nanocellulose has been growing. Nanocellulose has various applications ranging from composite reinforcement to rheological modifiers. Recently, nanocellulose has been shown to have great potential in flexible printed electronics applications.