Finishing and polishing systems influence the roughness and color stability of acrylic and bis-acryl composite resins.

Background: To evaluate the effect of different finishing and polishing systems on the surface roughness and color changes of bis-acryl (Protemp 4 - 3M ESPE- St. Paul, USA; Structur 3 - Voco, Cuxhaven, Germany) and chemically activated acrylic materials (Duralay - Reliance, SP, Brazil).

Material And Methods: Specimens (10 x 2 mm) thick were prepared for each material.

Effect of endodontic sealers on push-out bond strength of CAD-CAM or prefabricated fiber glass posts.

This study aimed to evaluate the effect of endodontic sealer (ES) on bond strength (BS) of prefabricated or milled-CAD-CAM (computer-aided design and computer-aided manufacturing) glass-fiber-posts (GFP). Canals of 90 single-rooted teeth were prepared for filling by the single-cone technique with gutta-percha and one of the following ES: AH Plus (epoxy resin), Endofill (zinc-oxide and eugenol), and Bio-C Sealer (calcium-silicate). After post-space preparation, tooth-specimens were equally divided in half according to type of GFP to be used.

Wet-bonding technique with ethanol may reduce protease activity in dentin-resin interface following application of universal adhesive system.

Background: Greater degradation of the hybrid layer is expected when a universal adhesive system is used, especially in the conventional application strategy. Therefore, it would important to evaluate the effect of the ethanol (ETH) and a potential matrix protease inhibitor (caffeic acid phenethyl ester/ CAPE) to maximize the ability to achieve stable dentin bond strength. The aim of this study was to evaluated the effect of ETH on a wet-bonding technique, and dentin pretreatments with different concentrations of CAPE in ethanolic solution, followed by application of a universal adhesive system (Single Bond Universal) to inhibit proteolytic activity.

Titanium dioxide nanotubes in a hydrogen peroxide-based bleaching agent: physicochemical properties and effectiveness of dental bleaching under the influence of a poliwave led light activation.

Objectives: The effects of different concentrations of titanium dioxide (TiO) into 40% hydrogen peroxide (HP) were evaluated as regards the effectiveness of dental color change either associated with activation by polywave LED light or not.

Materials And Methods: TiO (0, 1, 5, or 10%) was incorporated into HP to be applied during in-office bleaching (3 sessions/40 min each). Polywave LED light (Valo Corded/Ultradent) was applied or not in activation cycles of 15 s (total time of 2 min).

Implant-Abutment Misfit after Cyclic Loading: An In Vitro Experimental Study.

This study aimed to evaluate the influence of thermomechanical cycling (TMC) and type of abutment on the misfit and compressive strength of the implant−abutment interface. Forty 3.75-mm external hexagon implants with 25° angled abutments were divided into four groups (N = 10).

The use of desensitizing agents during in-office bleaching might not decrease tooth bleaching sensitivity: a randomized clinical trial.

Background: Due to controversial results in relation to the influence of desensitizing agents on sensitivity during bleaching, the present study evaluated the degree of tooth bleaching sensitivity, color change, and patient acceptability of desensitizing agents containing potassium nitrate/sodium fluoride (PNF) or nanostructured calcium phosphate (N) associated with in-office bleaching with 35% hydrogen peroxide (HP).

Materials And Methods: Seventy-five patients were randomly distributed into three groups (n = 25): 1) Group W - in-office bleaching (Whiteness HP Maxx - three sessions of 45 min); 2) Group WD - associated with PNF desensitizing gel (Desensibilize KF 2%) applied for 10 min before each session; 3) Group WDN - associated with N desensitizing paste (Desensibilize Nano P) applied after bleaching for 5 min. The degree of sensitivity and patient acceptability of the desensitizing treatments were evaluated using a visual analog scale.

Effect of whitening dentifrices on color, surface roughness and microhardness of dental enamel in vitro.

Purpose: To evaluate the color, surface roughness and microhardness of human dental enamel subjected to brushing with whitening dentifrices.

Methods: The enamel samples (4 x 4 x 2 mm) were darkened using 0.2% chlorhexidine and black tea, and were randomly divided into seven groups (n= 15) for brushing cycles with only water; control; conventional dentifrice (Colgate Maximum Anticaries Protection); dentifrice containing 2% hydrogen peroxide (Colgate Luminous White Advanced); dentifrice containing sodium tripolyphosphate (Sensodyne True White); dentifrice containing activated charcoal (Black is White); and dentifrice containing blue covarine (Close Up White Now).

Assessment of frictional resistance and surface roughness in orthodontic wires coated with two different nanoparticles.

Several mechanical and biological factors may change the orthodontic wire frictional resistance (FR). Titanium dioxide (TiO ) and silica dioxide (SiO ) nanoparticle (NP) coatings may be used to improve the characteristics of materials, reducing FR between archwire and bracket. This in vitro study aimed to evaluate the FR of orthodontic wires with and without coating in both dry and wet environments and measure the surface roughness (SR).

Phenolic extract of Libidibia ferrea inhibits dentin endogenous enzymatic activity depending on the adhesive system strategy.

This study evaluated the influence of Libidibia ferrea (Lf) extract used as dentin pretreatment on the resin-dentin bond strength stability and dentin endogenous enzymatic activity. The phytochemical profile (PP) of the Lf extract was evaluated by liquid chromatography; particle size, polydispersity index (PdI), and zeta potential (ZP) were evaluated by dynamic light scattering. The tested groups were ER-Scotchbond Universal (SBU) in the etch-and-rinse (ER) mode; ERLf-SBU in the ER mode + Lf after etching; SE- SBU in the self-etch (SE) mode; and LfSE-Lf before SBU in the SE mode.

Biomechanical behavior of atrophic maxillary restorations using the all-on-four concept and long trans-sinus implants: A finite element analysis.

Maxillary bone atrophy with a considerable amount of pneumatization and anterior expansion of the maxillary sinus might be a situation limiting oral rehabilitation with osseointegrated implants. Therefore, the present study aimed to biomechanically evaluate two rehabilitation techniques for maxillary bone atrophy: all-on-four and long trans-sinus implants. Two three-dimensional models consisting of atrophic maxilla with four implants were simulated.

Polyphenol-enriched extract of Arrabidaea chica used as a dentin pretreatment or incorporated into a total-etching adhesive system: Effects on bonding stability and physical characterization.

The aim of this paper was to evaluate the physical properties and the long-term bond strength of a 2.5% polyphenol-enriched extract of Arrabidaea chica (AC) incorporated into both the phosphoric acid and the primer of a three-step total-etch adhesive, or into an aqueous solution as a dentin pretreatment. Fifty dentin surfaces received the treatments (n = 10): CON (control) - application of the three-step adhesive system (Adper Scotchbond Multipurpose, 3M ESPE); WAT - distilled water used as a pretreatment after dentin etching and before application of the adhesive system; ACPA - AC incorporated into the phosphoric acid; ACW - dentin pre-treatment with AC incorporated into an aqueous solution after etching; ACP - AC incorporated into the primer.

Multibenefit Desensitising/Whitening Toothpastes: A Study on Abrasion and Permeability of Root Dentine.

Purpose: This study investigated the role of desensitising-only and desensitising/whitening versions of arginine and calcium carbonate-containing (ACC) and calcium sodium phosphosilicate-containing (CSPS) toothpastes on surface loss and permeability of root dentine.

Materials And Methods: Slabs of human root dentine were embedded and exposed to citric acid solution to create a lesion resembling hypersensitive dentine. Sixty specimens were divided into six groups and exposed to slurries made with ACC (Colgate Sensitive Pro-Relief) and CSPS (Sensodyne Repair & Protect) toothpastes, in their desensitising or desensitising/whitening versions, an ordinary toothpaste (Crest Cavity Protection) or distilled water (DI).

Lubricating conditions: effects on friction between orthodontic brackets and archwires with different cross-sections.

Objective: This study investigated the effect of the condition of lubrication on the friction between brackets and NiTi archwires of different rounded cross-sections.

Methods: Brackets (Roth, GAC) were affixed to a device connected to a universal testing machine into which segments of archwire were placed (NiTi, Nitinol, GAC) with cross-sections of 0.012-in, 0.

TiF4 Incorporated into a Self-etching Primer in Different Concentrations: Antimicrobial Properties and Effects on Demineralisation Inhibition Around the Restoration/Enamel-Dentin Interface.

Purpose: To apply titanium tetrafluoride (TiF4) in an aqueous solution or incorporated into the primer of a self-etching adhesive (Clearfil SE Bond) as dentin pre-treatment and evaluate its antimicrobial effect, determine the minimum bactericidal concentraion (MBC) against Streptococcus mutans and Lactobacillus casei and analyse its potential to inhibit the development of carious lesions at the restoration interface.

Materials And Methods: For MBC, an aqueous solution or primer with different concentrations (in %) of TiF4 were used (from 0.0 to 4.

Effect of epigallocatechin-3- gallate solutions on bond durability at the adhesive interface in caries-affected dentin.

Hydrolytic and enzymatic degradation by matrix metalloproteinases (MMPs) reduces the durability of composite resin restorations on caries-affected dentin (CAD). The use of MMP inhibitors such as epigallocatechin-3-gallate (EGCG) could increase the longevity of the bond to dentin. This study aimed to evaluate the use of EGCG at different aqueous concentrations on the resin-dentin microtensile bond strength (μTBS), fracture pattern and nanoleakage (NL) in immediate (IM) time interval and after 12-months of water storage (1Y) when using a two-step etch-and-rinse adhesive system on CAD.

Effect of Fiber Post Cementation Timing on the Bond Strength of Resin Cements in Epoxy Resin-Obturated Canals.

This study evaluated the influence of timing after endodontic treatment and type of resin cement used on the bond strength of fiber posts to epoxy resin-obturated canals. A total of 80 bovine incisor roots were divided into four groups (n = 20). Glass fiber posts were cemented at two different times, immediately or 7 days after endodontic treatment, using either a dual-curing resin cement (RelyX ARC, 3M ESPE) or a self-adhesive resin cement (RelyX U200, 3M ESPE).

Changes to Glazed Dental Ceramic Shade, Roughness, and Microhardness after Bleaching and Simulated Brushing.

Purpose: To evaluate shade stability, surface roughness, microhardness, and compressive strength of a glazed feldspathic ceramic subjected to bleaching and simulated brushing.

Materials And Methods: Eighty-eight glazed feldspathic ceramic specimens were made from microparticulate leucite and divided into eight groups (n = 10). The whitening products used were: Opalescence Trèswhite Supreme (Ultradent), Opalescence®\ PF 15% (Ultradent), and Oral-B 3D White Whitestrips.

Resin-dentin bond stability and physical characterization of a two-step self-etching adhesive system associated with TiF.

Objectives: To evaluate the bond strength to superficial (SD) and deep (DD) dentin after the use of 2.5% (T2.5%) or 4% (T4%) titanium tetrafluoride (TiF) in aqueous solution as a dentin pretreatment, or when incorporated into the primer (T2.

Effect of green tea extract on bonding durability of an etch-and-rinse adhesive system to caries-affected dentin.

Objective: Green tea extract has been advocated as a matrix metalloproteinase (MMP) inhibitor; however, its effect on bond durability to caries-affected dentin has never been reported. Thus, the aim of this in vitro study was to evaluate the effect of two MMP inhibitors (2% chlorhexidine and 2% green tea extract), applied after acid etching, on bond durability of an etch-and-rinse adhesive system to caries-affected dentin.

Material And Methods: Occlusal enamel was removed from third molars to expose the dentin surface, and the molars were submitted to a caries induction protocol for 15 days.

In Vitro Effects of 2.5% Titanium Tetrafluoride on Streptococcus Mutans and Lactobacillus Casei in Dentin Followed by Self-Etching Adhesive Systems.

The aim was to evaluate the effect of a 2.5% titanium tetrafluoride (TiF4) solution followed by self-etching adhesives against Streptococcus mutans/Sm and Lactobacillus casei/Lc. Four cylindrical-shaped cavities were performed on each dentin surface of 40 third molars and contaminated with Sm or Lc.

Influence of an arginine-containing toothpaste on bond strength of different adhesive systems to eroded dentin.

The aim of this study was to evaluate the bond strength of different adhesive systems to eroded dentin following toothbrushing with an arginine-containing toothpaste. Sixty standardized 3 × 3 × 2-mm fragments of root dentin (n = 10) were prepared. After all surfaces except the buccal surfaces were impermeabilized, specimens were subjected to an erosive wear protocol and stored for 24 hours at 37°C.

Antimicrobial Potential of Papain Chemomechanical Agent on Streptococcus Mutans and Lactobacillus Casei Followed by the Use of Self-Etching Adhesive Systems.

Objective: This study evaluated the antimicrobial effect of papain-based gel (Papacárie/ P) followed by self-etching adhesive systems with MDPB monomer (Clearfil Protect Bond/ PB) and without (Clearfil SE Bond/ Cl) on Streptococcus mutans (Sm) and Lactobacillus casei (Lc).

Study Design: The dentin of twenty human teeth was exposed to prepare four cylindrical cavities in each tooth. The cavities were incubated with Sm or Lc.

Rinsing with antacid suspension reduces hydrochloric acid-induced erosion.

Objective: Mouthrinsing with antacids, following erosive episodes, have been suggested as a preventative strategy to minimize tooth surface loss due to their neutralizing effect. The purpose of this in situ study was to evaluate the effect of an antacid suspension containing sodium alginate, sodium bicarbonate and calcium carbonate in controlling simulated erosion of enamel of intrinsic origin.

Design: The experimental units were 48 slabs (3×3×2mm) of bovine enamel, randomly divided among 12 volunteers who wore palatal appliances with two enamel slabs.

Influence of translucence/opacity and shade in the flexural strength of lithium disilicate ceramics.

Background: Lithium disilicate ceramic system consists of glass ceramic ingots with different grades of translucence which may influence its flexural strength.

Aims: To assess the three-point flexural strength of the different lithium disilicate-based ceramic ingots (IPS e.max Press/Ivoclar Vivadent) with different levels of translucence and shade.

In vitro evaluation of calcium and phosphorus concentrations in enamel submitted to an in-office bleaching gel treatment containing calcium.

The aim of this in vitro study was to evaluate the calcium and phosphorus concentrations in enamel surfaces before, during, and after treatment with in-office 35% hydrogen peroxide bleaching agents with 2% calcium gluconate (WCa) or without calcium gluconate (W). Twenty sound human third molars were divided into 2 groups of 10. The bleaching agents were applied to the tooth surfaces in accordance with the manufacturer's instructions: WCa, 40 minutes per day at 3 sessions with 7-day intervals; W, 3 × 15 minutes per day at 3 sessions with 7-day intervals.